Nano-Sized Additive Synthesis for Lubricant Oils and Compatibility Tests with After-Treatment Catalysts
Technical Paper
2011-24-0101
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Molybdenum sulfide nanoparticles have been successfully obtained, for lubricant applications, by means of a wet chemical synthesis in an aqueous solution employing ammonium molybdate, citric acid and ammonium sulfide as the reactants. Some molybdenum-citrate complexes were formed and they reacted with the ammonium sulfide to form MoS₂ nanoparticles. Mo:citrate molar ratio was identified as being the most relevant of the synthesis parameters that affected the phase and morphology of the final products. The optimized nanopowders were softly agglomerated and amorphous, with a mean size of the primary particles of about 30 nm. The compatibility between the thus obtained MoS₂ nanopowders and some commercial after-treatment catalysts for diesel vehicle engines was tested. Diesel oxidation, soot combustion and ammonia-SCR de-NOx catalysts were considered as were the possible effects on the catalytic activity and their possible reaction to the MoS₂ additive. In general, the presence of the MoS₂ nano-additive has been demonstrated to slightly decrease the catalytic performance of the commercial catalysts, especially for the diesel oxidation and SCR ones. The chemical-physical analyses did not detect any interaction between the catalysts and nano-additives or any decrease in the specific surface areas of the catalysts.
Recommended Content
Authors
Topic
Citation
Fino, D., Deorsola, F., Bensaid, S., and Russo, N., "Nano-Sized Additive Synthesis for Lubricant Oils and Compatibility Tests with After-Treatment Catalysts," SAE Technical Paper 2011-24-0101, 2011, https://doi.org/10.4271/2011-24-0101.Also In
References
- Rapoport, L. Feldman, Y. Homyonfer, M. Cohen, H. Sloan, J. Hutchison, J.L. Tenne, R. 1999 Inorganic fullerene-like material as additives to lubricants: structure-function relationship Wear 225-229 2 975 982
- Rapoport, L. Leshchinsky, V. Lapsker, I. Volovik, Y. Nepomnyashchy, O. Lvovsky, M. Popovitz-Biro, R. Feldman, Y. Tenne, R. 2003 Tribological properties of WS 2 nanoparticles under mixed lubrication Wear 255 7-12 785 793
- Wang, H.D. Xu, B.S. Liu, J.J. Zhuang, D.M. 2005 Characterization and anti-friction on the solid lubrication MoS 2 film prepared by chemical reaction technique Sci. Tech. Adv. Mat. 6 5 535 539
- Tenne, R. Margulis, L. Genut, M. Hodes, G. 1992 Polyhedral and cylindrical structures of tungsten disulphide” Nature 360 444 446
- Margulis, L. Salitra, G. Tenne, R. Talianker, M. 1993 Nested fullerene-like structures Nature 365 113 114
- Hershfinkel, M. Gheber, L.A. Volterra, V. Hutchison, J.L. Margulis, L. Tenne, R. 1994 Nested Polyhedra of MX2 (M=W, Mo; X=S, Se) Probed by High-Resolution Electron Microscopy and Scanning Tunneling Microscopy J. Am. Chem. Soc. 116 1914 1917
- Yacaman, M.J. Lorez, H. Santiago, P. Galvan, D.H. Garzon, I.L. Reyes, A. 1996 Studies of MoS 2 structures produced by electron irradiation Appl. Phys. Lett. 69 8 1065 1067
- Parilla, P.A. Dillon, A.C. Jones, K.M. Riker, G. Schulz, D.L. Ginley, D.S. Heben, M.J. 1999 The first true inorganic fullerenes? Nature 397 114
- Tian, Y. He, Y. Zhu, Y.F. 2003 Hydrothermal synthesis of fine MoS 2 crystals from Na 2 MoO 4 and KSCN Chem. Lett. 8 768 769
- Tian, Y. Zhao, J. Fu, W. Liu, Y. Zhu, Y. Wang, Z. 2005 A facile route to synthesis of MoS 2 nanorods Mater. Lett. 59 3452 3455
- Duphil, D. Bastide, S. Lévy-Clément, C. 2002 Chemical synthesis of molybdenum disulfide nanoparticles in an organic solution J. Mater. Chem. 12 8 2430 2432
- Uzcanga, I. Bezverkhyy, I. Afanasiev, P. Scott, C. Vrinat, 2005 Sonochemical Preparation of MoS 2 in Aqueous Solution: Replication of the Cavitation Bubbles in an Inorganic Material Morphology M. Chem. Mater. 17 3575 3577
- Chang, L.X. Yang, H.B. Li, J.X. Fu, W.Y. Du, Y.H. Du, K. Yu, Q.Y. Xu, J. Li, M.H. 2006 Simple synthesis and characteristics of Mo/MoS 2 inorganic fullerene-like and actinomorphic nanospheres with core-shell structure Nanotechnology 17 3827 3831
- Li, X.L. Ge, J.P. Li, Y.D. 2004 Atmospheric Pressure Chemical Vapor Deposition: An Alternative Route to Large-Scale MoS 2 and WS 2 Inorganic Fullerene-like Nanostructures Chem. Eur. J. 10 23 6163 6171
- Etzkorn, J. Therese, A.H. Rocker, F. Zink, N. Kolb, U. Tremel, W. 2005 Metal-Organic Chemical Vapor Depostion Synthesis of Hollow Inorganic-Fullerene-Type MoS 2 and MoSe 2 Nanoparticles Adv. Mater. 17 19 2372 2375
- Marchand, K.E. Tarret, M. Lechaire, J.P. Normand, L. Kasztelan, S. Cseri, T. 2003 Investigation of AOT-based microemulsion for the controlled synthesis of MoSx nanoparticles: an electron microscopy study Colloid Surface A 214 239 248
- Cizaire, L. Vacher, B. Le Mogne, T. Martin, J.M. Rapoport, L. Margolin, A. Tenne, R. 2002 Mechanisms of ultra-low friction by hollow inorganic fullerene-like MoS2 nanoparticles Surf. Coat. Technol. 160 282 287
- Joly-Pottuz, L. Martin, J.M. Dassenoy, F. Belin, M. Montagnac, R. Reynard, B. 2006 Pressure-induced exfoliation of inorganic fullerene-like WS2 particles in a Hertzian contact J. Appl. Phys. 99 023524 023528
- Lahouij, I. Dassenoy, F. De Knoop, L. Martin, J.M. Vacher, B. 2011 In-situ TEM observation of the behavior of an individual fullerene-like MoS2 nanoparticle in a dynamic contact Tribo. Lett. 42 2 133 140
- Gavi, E. Marchisio, D.L. Barresi, A.A. 2008 On the importance of mixing for the production of nano-particles J. Dispersion Sci. Technol. 29 548 554
- Zaccone, A. Gaebler, A. Maass, S. Marchisio, D.L. Kraume, M. 2007 Drop breakage in liquid-liquid stirred dispersions: Modelling of single drop breakage Chem. Eng. Sci. 62 6297 6307
- Aridi, T.N. Al-Daous, M.A. 2009 HDS of 4,6-dimethyldibenzothiophene over MoS 2 catalysts supported on macroporous carbon coated with aluminosilicate nanoparticles Appl. Catal. A 359 180 187
- Russo, N. Fino, D. Saracco, G. Specchia, V. 2005 Studies on the redox properties of chromite perovskite catalysts for soot combustion J. Catal. 229 2005 459 469
- Van Setten, B.A.A.L. Makkee, M. Moulijn, J.A. 2001 Science and technology of catalytic diesel particulate filters Catal. Rev. - Sci. Eng. 43 489 564
- Samotus, A. Kanas, A. Dudek, M. Grybos, R. Hodorowicz, E. 1991 1:1 Molybdenum(VI) citric acid complexes Trans. Met. Chem. 16 495 499
- Stevens, G.C. Edmonds, T. 1977 Catalytic activity of the basal and edge planes of molybdenum disulphide J. Less-Common Metals 54 321 330
- Zinggs, D.S. Makovsky, L.E. Tischer, R.E. Brown, F.R. Hercules, D.M. 1980 A surface spectroscopic study of molybdenum-alumina catalysts using x-ray photoelectron, ion-scattering, and Raman spectroscopies J. Phys. Chem. 84 22 2898 2906