Weld Read-Through Defects in Laser Transmission Welding
Technical Paper
2011-01-0476
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
In Laser Transmission Welding (LTW), a laser beam passes through a transparent part and is dissipated as heat in an absorbent material through the use of laser-absorbing pigments such as carbon black (CB). This energy is then conducted further into both parts. Melting and subsequent solidification occur at the interface causing a weld to form between the two parts. Gluing or welding structures to the back of automotive Class-A panels often results in the appearance of undesirable surface deformations on the Class-A side. Through control of the laser welding and material parameters, it may be possible to use contour LTW as a means of joining structures to the back of absorbent Class-A panels without creating these unwanted surface defects. A series of lap welds was made using a range of CB levels and laser powers. A profilometer was used to measure the size and shape of the defects generated on the surface of the black part. Two types of defects were observed: ribs and sink marks. It was observed that lower powers combined with higher carbon black levels generally resulted in smaller defects. The type of defect depended on the boundary conditions between the two parts and the flow of polymer that had thermally expanded during welding (flash). If weld flash flowed into gaps between the two plates, rib defects were always observed. If flash flowed elsewhere and no gaps existed between the plates, sink marks occurred. A simple mechanism is proposed to explain these observations.
Recommended Content
Technical Paper | Laser Joining Technologies for Dissimilar Material Combinations |
Technical Paper | Clearance Control Coatings - Low Cost, Abradable, Lubricious |
Technical Paper | Powder Metallurgy of High Density Helical Gears |
Authors
Citation
Bates, P., Zak, G., and Cao, X., "Weld Read-Through Defects in Laser Transmission Welding," SAE Technical Paper 2011-01-0476, 2011, https://doi.org/10.4271/2011-01-0476.Also In
References
- Hoyden, K. Engelmann, P. “Smoke and mirrors: Hiding sink in plain sight” ANTEC 2008 Society of Plastics Engineers 703 707
- Pallante, M. “texturing adds product value at low cost” Plastics Engineering 40 2 Feb 1984 45 47
- Cao, X. “Weld read-through defects in laser transmission welding” Queen's University M.A.Sc. Thesis 2010
- Potente, H. Korte, J. Becker, F. “Laser transmission welding of thermoplastics: analysis of the heating phase” ANTEC 1998 1022 1025
- Chen, M. Zak, G. Bates, P.J. “Laser absorption coefficient measurement of amorphous polymers for laser transmission welding” ANTEC 2006 2291 2295
- Grewell, D.A. Benatar, A. Park, J.B. Plastics and Composites Welding Handbook Hanser Gardner 2003
- www.matweb.com 8 January 2011
- Chen, M. Zak, G. Bates, P. Baylis, B. et al. “Method of Evaluating Shear Strengths in Contour Laser Transmission Welding,” SAE Technical Paper 2007-01-0571 2007 10.4271/2007-01-0571
- Operating manual for the ROFIN DL×16 Industrial Diode Laser 2003
- Chen, M. Zak, G. Bates, P.J. “Non-contact method for estimating contour laser transmission welding start-up conditions” IIW 2007 2 5
- Chen, M. Zak, G. Bates, P.J. “Estimating contour Laser Transmission Welding start-up conditions using a novel non-contact method,” Welding in the World, IIW-1912-08 52 11/12 Nov Dec 2008